were determined according to the GOST 4651-78 on an FP-100 testing machine. 

- the study of microhardness of the obtained organoplastics was carried out using 

the device PMT-3M;  

- coefficient of friction and weight wear were determined under conditions of 

friction without greasing on the friction disk machine at the pressure of 0,6 MPa, 
sliding speed of 1 m/s. The friction path was 1000 m. OP samples had cylindrical shape 
=10, h=12 mm; Steel 45 (45-48 HRC, R

a

=0,16-0,32 μm) was used as a counterbody. 

The coefficient of friction was determined by the formula: 

������=

������

1

+������

2

������

, 

where F

1

 is the friction force of the examined sample; F

2

 is the loss that occurs 

during the rotation of the lever on the tips in horizontal plane. The accuracy of friction 
force measurement was 5%; N is the normal load on the sample. 

The wear of the samples was determined by the gravimetric method on the 

analytical VLR - 200balance (GOST 24104 - 80) with an accuracy of up to 0,0001 g.  
The intensity of linear wear І

h

 was taken as the main engineering characteristic

 

of the 

wear process. It is expressed by the ratio: 

������

ℎ

=

������

������

������

∙

������������

������

������

∙������������

������

, 

where G is the value of weight wear; ρ

Т

 is the density of the wear material; A

a

 is 

nominal contact area; L is the path of friction. 

������=

������

������

������

������

, 

where A

T

 is nominal friction area. 

It was taken λ=1, i.e the wear of the body, all points of the friction surface of 

which are constantly in contact, was considered. 

The viscosity of phenol-formaldehyde binder was determined with the VZ-4 

viscometer at the room temperature. 

The dry residue and gel time was determined according to the GOST 901-78. 
Research on the heat resistance of organoplastics. The materials behavior is 

characterized by heat resistance while heating. The main method for determining heat 
resistance is thermogravimetric analysis (TGA). Samples of developed OP were 
subjected to the thermal analysis. The heat resistance of organoplastics (tab. 6,7 and 
Fig. 2,3) is determined by both the nature of thermosetting matrix and the nature of 
fibrous fillers and the filling degree of composites. 

Processing of thermogravimetric analysis (TGA) curves, which are presented on 

Fig. 2, showed sufficiently high heat resistance of the developed organoplastics based 
on PFR (LBS-1), especially in the case of 70 mass.% polysulfonamide Tanlon fiber 
(tab. 6). 

- 429 -