NACE TM 0284 method, "blistering" and brittle cracking in the structure of specimens 
of 06Cr1-U steel tubes were absent (СLR = 0, CTR = 0), the rate of their corrosion was 
0.29-0.30 mm/yr. It is worth noting that according to the published data [22, 23], 
corrosion rate of 20CrV steel pipes can reach 0.8 mm/yr, and more than 2 mm/yr for  
steel 20 tubes under such conditions. API 5L and API 5CT standards also allow 
presence of brittle cracks in the tube metal after testing for HC with a CLR 

characteristic (relative length of brittle cracks)  15 %. 

 

 

 

Figure

 7. Cathode polarization curves 

of 

06Cr1-U steel (1) and 20 steel (2) in a solution 

of 1N H

2

SO

4

+1.5 g/l CS (NH

2

)

2

 

Figure 8. Change of I

k

 in time in pipes of 06Cr1-U 

steel (1 and 2) and 20 steel (3 and 4) before operation 

(1 and 3) and after operation (2 and 4)  

 
 Long-term field tests (for more than 20 years till now) of a pilot batch of 06Cr1-U 

steel tubes were conducted at Anastasivsk field of Okhtyrkanaftogaz NGVU which is 
characterized by the highest corrosiveness of stratal and sewage water (see Table 2). The 
experimental batch of 06Cr1-U steel tubes is operated there as an industrial pipeline for 
pumping highly mineralized stratal water without corrosive damage. Inspections of the 
pipeline after 3, 6.5 and 10 years have shown a decrease in time of the average rate of 
corrosion of tubes (from 0.052 mm/yr after 3 years to 0.02 mm/yr after 10 years of 
operation, i.e. 2.6 times) and elevated (up to 3 %) chromium content in the oxide film 
formed on their surface. Alongside with this, during 6.5 years of observations conducted at 
the fields of Okhtyrkanaftogaz NGVU, more than 2000 through perforations caused by 
corrosion occurred in industrially operated steel 20 tubes according to GOST 8732 (in both 
the tube body and the welded joints). 

The results of testing of experimental 06Cr1-U steel tubes during 80 days (2.7 months) 

at the PermSRІnafta LLC (North Urals, Russia) in corrosive highly mineralized stratal 
water which in addition to chlorides and other corrosive components contained hydrogen 
sulfide (up to 45 mg/l) also showed significantly higher corrosion resistance of oil and gas 
line tubes of 06Cr1-U steel as compared to with steel 20 tubes. It is evident from the above 

- 451 -