was discovered that, independently of the fact whether the VIAC films are present or 
absent on the steel surface, the rate of the cathodic processes is much higher than the 
rate of anodic processes (Fig. 6).These dependences of the current density on the 
electrode potentials indicate the presence of fairly complicated multistage processes 
under the conditions of cathodic and anodic polarization of steel. Both the cathodic 
slopes and the anodic slopes do not change obviously, which indicates that the 
mechanism of the corrosion reaction does not change and the corrosion reaction is 
inhibited by a simple adsorption mode. 

 

 

 

Figure 5. SEM images of polished steel (a) and APE SAM modified steel after 48 h. 

 

Figure 6. Potentiodynamic polarization curves of mild steel in 0.5 М Na

2

SO

4

 without 

(1) and with film formed after 12 (2) 24 (2); 48 (4) and 72 (5) h in the vapor phase. 

Noticeably, the plant extract is a mixture of various components, which results in 

the complex inhibitive mechanism. It is rather difficult to determine what components 
present in plant extract create their relatively high ability to inhibit corrosion. However, 
it remains unknown what molecules of vapour-phase of 2-propanol pomaces the 
apricot extract are adsorbed on the steel surface and provides inhibition 

- 1449 -