a 

b 

c 

  

 

 

 

d 

e

 

Figure 2. Images of electron microscopy of the boundary layer of metal-

containing polymers, filled with: a) Al х10000; b) Cu, х10000; c) Bronze, x6000;  

d) Ni, х10000; e) Ti, х6000 

 

Within the interfacial layer polymer – filler phenylone macromolecules are 

straightened and aggregate into the oriented fibrillar structures around the filler 
particles (Fig. 3). The destruction of all the filled systems occurs by the adhesive – 
cohesive mechanism; on the surface of the polymer particles individual globules are 
visible. At the same time, at a very big distance from the interface boundary, the 
globular structure of the binder, the sizes of the globules and their packing density 
remain the same, being characteristic of the initial polymer. 

 

 

 

 

  

a 

b 

c 

  

 

 

  

d 

e

 

Figure 3. Images of electron microscopy of the interfacial layer of metal-

containing polymers, filled with: a) Bronze, x6000; b) Cu, х8000; c) Ni, х10000;  

d) Ti, х6000; e) Al, х6000 

- 1618 -