Figure 3.2. Dependence of eutectoid component amount in bronze BrA9Zh3L 

structure vs. zinc content 

Source: measured and calculated by the authors 

 
In addition to eutectoid component amount growing (12,47 ... 58,02%), formation 

of eutectoid structures with two different morphological types has been recorded. 
Figure 3.3 illustrates the fact that this occurs from concentration 0,2 wt. % Zn in alloy. 

a 

 

b 

 

c 

 

d 

 

 

a – 0,2 %Zn (×500), b – 2,50 %Zn (×500), c. d – 4,7%Zn (×1000) 

Figure 3.3. Results of eutectoid component substructure microstructural study 

of bronze BrA9Zh3L with different zinc content

 

Source: borrowed by the authors according to source [24] 

 