Present work authors in [24] article have suggested that such components have 

not only different morphologies, but also origin genesis, associated with zinc 
appearance in Cu-Al-Fe system. Measurement of components concentration in studied 
bronze samples α-Cu solid solution crystals have been carried out by energy-dispersive 
analysis method. Examples of quantitative components microanalysis are shown in 
Figure 3.4. Measurement results are presented in Table 3.1. 

 

a 

 

 

b 

 

 

a – Spectrum 2, b – Spectrum 3 

Figure 3.4. Results of bronze BrA9Zh3L quantitative X-ray energy-dispersive 

analysis 

Source: analyzed by the authors 

 

Table 3.1 Energy-dispersive analysis results of elements content in α-Cu solid 

solution 

Spectrum № 

Components content, wt. % 

Aluminum 

Iron 

Zinc 

Σ=Al+Fe+Zn 

Cu 

Spectrum 1 

7.68 

1.25 

4.17 

13.10 

The base 

Spectrum 2 

8.06 

1.14 

4.00 

13.20 

Spectrum 3 

7.79 

1.28 

4.42 

13.49 

Spectrum 4 

8.08 

1.31 

4.19 

13.58 

Spectrum 5 

8.09 

1.29 

4.48 

13.86 

Spectrum 6 

7.35 

1.66 

4.90 

13.91 

Spectrum 7 

7.75 

1.63 

4.38 

13.76 

Spectrum 8 

7.72 

1.33 

4.47 

13.52 

Source: calculated and completed by the authors 
 